EVALUATION OF FATIGUE CRACK GROWTH DUE TO BENDING ON THE AUTOFRETTAGED CYLINDERS WITH EXTERNAL CRACK

Q: How can I download an article?

To download an article from SID, first log in to the site, search for the article title, and click on the 'Download Article' option.

Q: How can I download an ISI article?

To download an ISI article on SID, enter the keyword or article title in the search bar, view the relevant results, click on the desired article, and select the 'Download Article' option.

Q: How can I access the SID database?

To access the SID database, visit SID.ir, create an account, and log in to access scientific resources.

Q: Is downloading articles from SID free?

Some articles on SID are available for free, while others require payment. Details are specified on the article's page.

SEIFI RAHMAN; HAKIMI HOSSEIN

مرکز اطلاعات علمی Scientific Information Database (SID) - Trusted Source for Research and Academic Resources

Journal Paper

Paper Information

Journal: Modares Mechanical Engineering Year:2017 | Volume:16 | Issue:11 Page(s): 35-44

Download Full-Text

Persian Verion

View:

977

Download:

Cites:

Information Journal Paper

Title

EVALUATION OF FATIGUE CRACK GROWTH DUE TO BENDING ON THE AUTOFRETTAGED CYLINDERS WITH EXTERNAL CRACK

Author(s)

SEIFI RAHMAN | HAKIMI HOSSEIN | Issue Writer Certificate

Keywords

AUTOFRETTAGEQ1

EXTERNAL CRACKQ1

FATIGUE CRACK GROWTHQ2

BENDINGQ2

Abstract

In this study, fatigue growth of external surface cracks on the AUTOFRETTAGEd cylinders under BENDING is investigated. AUTOFRETTAGE is a process in which a thick-walled cylinder subjected to internal pressure with known amount, causing some portions on the inner zone of the cylinder deformed plastically. In this case, removing the pressure causes compressive residual stresses on the inner layers and tensile stresses on the outer wall. The goal is increasing the fatigue durability of the product by inducing residual compressive stresses into materials, but along with this, there are adverse tensile stresses which can decrease the life due to the outer defects. In this paper, the EXTERNAL CRACKs are in the forms of halfelliptical, semi-elliptical and semi-circle. Samples made by aluminum 2024 alloy. The cylinders were AUTOFRETTAGEd up to 40 and 60 percent. Cracks were located in circumferential direction and normal to cylinder axis. The numerical simulations were performed by finite element method. Experimental data and numerical results were compared. Results show that the number of load cycles to fracture, in the 60% AUTOFRETTAGEd cylinders are smaller than those for 40% and also smaller than the state without AUTOFRETTAGE. Distribution of stress intensity factor along the crack front is symmetric and crack grows in its initial plane which indicating the dominance of the first mode of failure during the crack growth.In all samples, after some steps of the growth, crack front transforms to the semi-elliptical shape until complete fracture.

Cites

No record.

References

No record.

Cite

APA: Copy

SEIFI, RAHMAN, & HAKIMI, HOSSEIN. (2017). EVALUATION OF FATIGUE CRACK GROWTH DUE TO BENDING ON THE AUTOFRETTAGED CYLINDERS WITH EXTERNAL CRACK. MODARES MECHANICAL ENGINEERING, 16(11 ), 35-44. SID. https://sid.ir/paper/178920/en

Vancouver: Copy

SEIFI RAHMAN, HAKIMI HOSSEIN. EVALUATION OF FATIGUE CRACK GROWTH DUE TO BENDING ON THE AUTOFRETTAGED CYLINDERS WITH EXTERNAL CRACK. MODARES MECHANICAL ENGINEERING[Internet]. 2017;16(11 ):35-44. Available from: https://sid.ir/paper/178920/en

IEEE: Copy

RAHMAN SEIFI, and HOSSEIN HAKIMI, “EVALUATION OF FATIGUE CRACK GROWTH DUE TO BENDING ON THE AUTOFRETTAGED CYLINDERS WITH EXTERNAL CRACK,” MODARES MECHANICAL ENGINEERING, vol. 16, no. 11 , pp. 35–44, 2017, [Online]. Available: https://sid.ir/paper/178920/en

Related Journal Papers