INTERFACE CHARACTERIZATION OF AL/CAST IRON COMPOSITE

Q: How can I download an article?

To download an article from SID, first log in to the site, search for the article title, and click on the 'Download Article' option.

Q: How can I download an ISI article?

To download an ISI article on SID, enter the keyword or article title in the search bar, view the relevant results, click on the desired article, and select the 'Download Article' option.

Q: How can I access the SID database?

To access the SID database, visit SID.ir, create an account, and log in to access scientific resources.

Q: Is downloading articles from SID free?

Some articles on SID are available for free, while others require payment. Details are specified on the article's page.

AKBARIFAR MEHDI; DIVANDARI MEHDI

Scientific Information Database (SID) - Trusted Source for Research and Academic Resources

Journal Paper

Paper Information

Journal: Journal of Science and Technology of Composites Year:2016 | Volume:3 | Issue:3 Page(s): 261-268

Download Full-Text

مرکز اطلاعات علمی Scientific Information Database (SID) - Trusted Source for Research and Academic Resources

Persian Verion

View:

1,071

Download:

Cites:

Information Journal Paper

Title

INTERFACE CHARACTERIZATION OF AL/CAST IRON COMPOSITE

Author(s)

AKBARIFAR MEHDI | DIVANDARI MEHDI | Issue Writer Certificate

Keywords

ALUMINUMQ2

CAST IRONQ2

INTERFACEQ2

INTERMETALLIC COMPOUNDQ2

GRAPHITEQ3

Abstract

In this article, INTERFACE characteristics of ALUMINUM and CAST IRON bimetal has been investigated. To reach an acceptable composite products, from two materials, INTERFACE characteristics needs to be investigated. ALUMINUM melt was poured, at 700 and 750oC, around cylindrical CAST IRON bars having melt/solid volume ratios of 3, 5 and 8, respectively. Optical and SEM microscopic observations showed that a reaction layer may form at the INTERFACE. This layer is composed of Fe2Al5 intermetallic which forms initially at the rough surface of the insert after making contact with molten metal. Microstructural analysis showed the increasing of temperature and the Vm/Vs ratio leads to formation of a thicker and more uniform intermetallic layer. Microhardness of the Fe2Al5 was 824 HV and the thickness of interaction layer varied from 5μm, for the sample produced at 700oC and 3 Vm/Vs, up to 20μm for the sample poured at 750oC and 8 Vm/Vs. A mechanism is suggested for nucleation and growth of this intermetallic layer and also GRAPHITE engulfment of gray CAST IRON, by ALUMINUM melt, at the INTERFACE of two metals.

Cites

No record.

References

No record.

Cite

APA: Copy

AKBARIFAR, MEHDI, & DIVANDARI, MEHDI. (2016). INTERFACE CHARACTERIZATION OF AL/CAST IRON COMPOSITE. JOURNAL OF SCIENCE AND TECHNOLOGY OF COMPOSITES (JSTC), 3(3), 261-268. SID. https://sid.ir/paper/251642/en

Vancouver: Copy

AKBARIFAR MEHDI, DIVANDARI MEHDI. INTERFACE CHARACTERIZATION OF AL/CAST IRON COMPOSITE. JOURNAL OF SCIENCE AND TECHNOLOGY OF COMPOSITES (JSTC)[Internet]. 2016;3(3):261-268. Available from: https://sid.ir/paper/251642/en

IEEE: Copy

MEHDI AKBARIFAR, and MEHDI DIVANDARI, “INTERFACE CHARACTERIZATION OF AL/CAST IRON COMPOSITE,” JOURNAL OF SCIENCE AND TECHNOLOGY OF COMPOSITES (JSTC), vol. 3, no. 3, pp. 261–268, 2016, [Online]. Available: https://sid.ir/paper/251642/en

Related Journal Papers