HOT CORROSION PROPERTIES OF IRON ALUMINIDE COATINGS PRODUCED VIA A TWO STAGES PROCESS ON PLAIN CARBON STEEL

Q: How can I download an article?

To download an article from SID, first log in to the site, search for the article title, and click on the 'Download Article' option.

Q: How can I download an ISI article?

To download an ISI article on SID, enter the keyword or article title in the search bar, view the relevant results, click on the desired article, and select the 'Download Article' option.

Q: How can I access the SID database?

To access the SID database, visit SID.ir, create an account, and log in to access scientific resources.

Q: Is downloading articles from SID free?

Some articles on SID are available for free, while others require payment. Details are specified on the article's page.

OMRANIAN MOHAMMADI PEIMAN; RAISZADEH RAMIN; SHAHVERDI HAMID REZA

مرکز اطلاعات علمی Scientific Information Database (SID) - Trusted Source for Research and Academic Resources

Journal Paper

Paper Information

Journal: METALLURGICAL ENGINEERING Year:2017 | Volume:20 | Issue:2 (66) Page(s): 109-120

Download Full-Text

Persian Verion

View:

471

Download:

Cites:

Information Journal Paper

Title

HOT CORROSION PROPERTIES OF IRON ALUMINIDE COATINGS PRODUCED VIA A TWO STAGES PROCESS ON PLAIN CARBON STEEL

Author(s)

OMRANIAN MOHAMMADI PEIMAN | RAISZADEH RAMIN | SHAHVERDI HAMID REZA | Issue Writer Certificate

Keywords

TIG SURFACE ALLOYINGQ2

HIGH TEMPERATURE OXIDATIONQ2

FE3AL COATINGQ2

Abstract

The isothermal high temperature corrosion behavior of an FE3AL COATING coated on plain carbon steel through tungsten inert gas (TIG) surface alloying with current of 40A was studied in the atmosphere of air. The specimens were tested at 700 and 900oC for 4–100 h. SEM, EDS and XRD analyses were utilized to study the oxidation behavior of the iron aluminide intermetallic coating. The weight gain data determined a parabolic rate law. The results also revealed that the initial scale formed on the coating was predominately q-Al2O3 which was substituted by a-Al2O3 after about 64 hours. The SEM observation and XRD results illustrated that at shorted times, when the q phase was stable, spalling was more usual while with the increase in the amount of the a phase the spalling decreased significantly. The EDS results confirmed the presence of aluminum oxide at shorted times and iron oxide at longer times.

Cites

No record.

References

No record.

Cite

APA: Copy

OMRANIAN MOHAMMADI, PEIMAN, RAISZADEH, RAMIN, & SHAHVERDI, HAMID REZA. (2017). HOT CORROSION PROPERTIES OF IRON ALUMINIDE COATINGS PRODUCED VIA A TWO STAGES PROCESS ON PLAIN CARBON STEEL. METALLURGICAL ENGINEERING, 20(2 (66) ), 109-120. SID. https://sid.ir/paper/112422/en

Vancouver: Copy

OMRANIAN MOHAMMADI PEIMAN, RAISZADEH RAMIN, SHAHVERDI HAMID REZA. HOT CORROSION PROPERTIES OF IRON ALUMINIDE COATINGS PRODUCED VIA A TWO STAGES PROCESS ON PLAIN CARBON STEEL. METALLURGICAL ENGINEERING[Internet]. 2017;20(2 (66) ):109-120. Available from: https://sid.ir/paper/112422/en

IEEE: Copy

PEIMAN OMRANIAN MOHAMMADI, RAMIN RAISZADEH, and HAMID REZA SHAHVERDI, “HOT CORROSION PROPERTIES OF IRON ALUMINIDE COATINGS PRODUCED VIA A TWO STAGES PROCESS ON PLAIN CARBON STEEL,” METALLURGICAL ENGINEERING, vol. 20, no. 2 (66) , pp. 109–120, 2017, [Online]. Available: https://sid.ir/paper/112422/en

Related Journal Papers