An Investigation on Effect of Austempeing Heat Treatment on The Erosion Behavior of Ductile Alloy Cast Iron

Q: How can I download an article?

To download an article from SID, first log in to the site, search for the article title, and click on the 'Download Article' option.

Q: How can I download an ISI article?

To download an ISI article on SID, enter the keyword or article title in the search bar, view the relevant results, click on the desired article, and select the 'Download Article' option.

Q: How can I access the SID database?

To access the SID database, visit SID.ir, create an account, and log in to access scientific resources.

Q: Is downloading articles from SID free?

Some articles on SID are available for free, while others require payment. Details are specified on the article's page.

Taheri Mohammad Masood; Alizaeh Mehdi; BAHRAMI ABBAS; Saebi Kamran

مرکز اطلاعات علمی Scientific Information Database (SID) - Trusted Source for Research and Academic Resources

Journal Paper

Paper Information

Journal: IRANIAN JOURNAL OF SURFACE SCIENCE AND ENGINEERING Year:2020 | Volume:- | Issue:45 Page(s): 15-24

Download Full-Text

Persian Verion

View:

439

Download:

Cites:

Information Journal Paper

Title

An Investigation on Effect of Austempeing Heat Treatment on The Erosion Behavior of Ductile Alloy Cast Iron

Author(s)

Taheri Mohammad Masood | Alizaeh Mehdi | BAHRAMI ABBAS | Saebi Kamran | Issue Writer Certificate

Keywords

ErosionQ1

Ductile ironQ1

Carbidic austempered ductile ironQ1

Austempering heat treatmentQ2

Abstract

In this research, the Erosion behavior of carbidic austempered Ductile iron and alloyed Ductile iron was studied and compared. For this purpose, cubic specimens with a size of 3*3*1 cm were prepared, and subsequently austempered. Microstructural characterization was carried out using optical microscopy and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). Hardness and surface roughness were measured prior to the Erosion test. Specimens underwent Erosion test at the angles of 30, 45, 60, 75, and 90 degrees. Diagrams depicting weight loss for different angles denote that the carbidic specimens show higher Erosion strength in all angels. Moreover, X-ray diffraction results from the surface of the carbidic specimens prior and after the Erosion test demonstrated that there is 38 percent residual austenite on the surface of the carbidic specimens after the Erosion test which provides evidence for the strain-induced transformation of austenite to martensite during Erosion test. Micro-hardness tests on the surface of the carbidic specimens after the Erosion test demonstrated an increase from 446 to 531 vickers due to the transformation. Moreover, as apparent from the SEM images, the dominant Erosion mechanism is cutting and ploughing at low (30-60 degrees) and high angles (60-90 degrees) is crack and micro crack, respectively.

Cites

No record.

References

No record.

Cite

APA: Copy

Taheri, Mohammad Masood, Alizaeh, Mehdi, BAHRAMI, ABBAS, & Saebi, Kamran. (2020). An Investigation on Effect of Austempeing Heat Treatment on The Erosion Behavior of Ductile Alloy Cast Iron. IRANIAN JOURNAL OF SURFACE SCIENCE AND ENGINEERING, -(45 ), 15-24. SID. https://sid.ir/paper/403557/en

Vancouver: Copy

Taheri Mohammad Masood, Alizaeh Mehdi, BAHRAMI ABBAS, Saebi Kamran. An Investigation on Effect of Austempeing Heat Treatment on The Erosion Behavior of Ductile Alloy Cast Iron. IRANIAN JOURNAL OF SURFACE SCIENCE AND ENGINEERING[Internet]. 2020;-(45 ):15-24. Available from: https://sid.ir/paper/403557/en

IEEE: Copy

Mohammad Masood Taheri, Mehdi Alizaeh, ABBAS BAHRAMI, and Kamran Saebi, “An Investigation on Effect of Austempeing Heat Treatment on The Erosion Behavior of Ductile Alloy Cast Iron,” IRANIAN JOURNAL OF SURFACE SCIENCE AND ENGINEERING, vol. -, no. 45 , pp. 15–24, 2020, [Online]. Available: https://sid.ir/paper/403557/en

Related Journal Papers