FLOW BEHAVIOR AND MICROSTRUCTURAL INVESTIGATION OF GTD 111 CAST NICKEL BASE SUPERALLOY DURING HOT PRESSURE TEST

Q: How can I download an article?

To download an article from SID, first log in to the site, search for the article title, and click on the 'Download Article' option.

Q: How can I download an ISI article?

To download an ISI article on SID, enter the keyword or article title in the search bar, view the relevant results, click on the desired article, and select the 'Download Article' option.

Q: How can I access the SID database?

To access the SID database, visit SID.ir, create an account, and log in to access scientific resources.

Q: Is downloading articles from SID free?

Some articles on SID are available for free, while others require payment. Details are specified on the article's page.

MOHAMMADPOUR M.; MOMENI A.

مرکز اطلاعات علمی Scientific Information Database (SID) - Trusted Source for Research and Academic Resources

Journal Paper

Paper Information

Journal: JOURNAL OF NEW MATERIALS Year:2018 | Volume:8 | Issue:3 (31) Page(s): 167-178

Download Full-Text

Persian Verion

View:

944

Download:

Cites:

Information Journal Paper

Title

FLOW BEHAVIOR AND MICROSTRUCTURAL INVESTIGATION OF GTD 111 CAST NICKEL BASE SUPERALLOY DURING HOT PRESSURE TEST

Author(s)

MOHAMMADPOUR M. | MOMENI A. | Issue Writer Certificate

Keywords

SUPERALLOYQ1

GTD-111Q1

HOT COMPRESSIONQ2

ACTIVATION ENERGYQ1

Abstract

To investigate the behavior of the SUPERALLOY deformation behavior of GTD 111 casting, the hot-pressure tests were carried out at a temperature range of 950-1100oC and strain rates of 1- 0.001 s-1. All of the flow curves showed a relatively linear tension increase to one peak point and then its descent to a strain of 0.5, and the region of steady state deformation with constant stress was not observed. This process was attributed to the control of dislocations by the dendritic structure and their amplification at peak point. Microstructural investigations showed that the hot work would break the structure of the dendritic network and create separate cells. An increase in the temperature of the hot work, resulted an increase in the decomposition of the structure and the achievement of larger cells coused by dissolution of broken dendritic particles. Also, with the increase in the rate of deformation at a given temperature, the decomposition rate of the dendritic network decreased and its elongation increased in the direction of the deformation. Using the fundamental constants of material, n, b and a were determined at the peak point. Also, with the help of the fundamental relationship of sinuses hyperbolic, the amount of ACTIVATION ENERGY at the peak and the strain of 0.4 samples was 947 kJ / mol and 890 kJ / mol, respectively. These results showed that the deformation ACTIVATION ENERGY decreases with increasing strain and breaking the dendritic structure into distinct cells.

Cites

No record.

References

No record.

Cite

APA: Copy

MOHAMMADPOUR, M., & MOMENI, A.. (2018). FLOW BEHAVIOR AND MICROSTRUCTURAL INVESTIGATION OF GTD 111 CAST NICKEL BASE SUPERALLOY DURING HOT PRESSURE TEST. JOURNAL OF NEW MATERIALS, 8(3 (31) ), 167-178. SID. https://sid.ir/paper/170031/en

Vancouver: Copy

MOHAMMADPOUR M., MOMENI A.. FLOW BEHAVIOR AND MICROSTRUCTURAL INVESTIGATION OF GTD 111 CAST NICKEL BASE SUPERALLOY DURING HOT PRESSURE TEST. JOURNAL OF NEW MATERIALS[Internet]. 2018;8(3 (31) ):167-178. Available from: https://sid.ir/paper/170031/en

IEEE: Copy

M. MOHAMMADPOUR, and A. MOMENI, “FLOW BEHAVIOR AND MICROSTRUCTURAL INVESTIGATION OF GTD 111 CAST NICKEL BASE SUPERALLOY DURING HOT PRESSURE TEST,” JOURNAL OF NEW MATERIALS, vol. 8, no. 3 (31) , pp. 167–178, 2018, [Online]. Available: https://sid.ir/paper/170031/en